(Originally posted by Semafore)
I'm talking GLEAM!: ULTRA_SHINY and Smooth rails can now be had with my 'WHAT box?" approach to this conductivity problem. An HO modeller since 1970, I know the problem WELL!
THIS IS A ONE-TIME PROCESS. DO ALL TRACK!!
1] On an appropiate-sized block, use 400 wet/dry paper to remove the extrusion milling left on the railheads. The block must span both rails.
2] Now use 600 or finer, repeat process.
3] Using an appropiate-sized STAINLESS-STEEL piece, apply moderate pressure and BURNISH the rails! The more you slide back and forth, the smoother and shinier the rails become! [ the GLEAM part ]. This is because you have removed the ridges, bumps, and pits. Burnishing helps seal pores with metal, eliminating traps for dirt and tarnish; almost like a MIRROR!
4] [For Bob H.] Use BLUE MAGIC or equivalent metal polish to deep-clean the remaining contaminates.
5] Last, buff the rails to your eye's content!
The shine is 5x more lusterous than just polish alone. The wax left behind is minimal, is not insulating, and virtually eliminates rail cleaning.
This is a process HOT OFF THE PRESSES! [Of my brain] I've only been at it 6 weeks with amazing results! {I just added the wax step today.} prior to that, though, the NS HO rails I'm guinea-pigging (300') sans wax STILL gleams today, with slight tarnishing, so I'm gonna wax 'em next!
I will also try some classic brass rail to see how that stands up.
AND REMEMBER; NO MORE ABRASIVES...EVER!!!!!!
Or you'll just ruin your mirror finish, and will have to gleam and wax AGAIN!
Dry-wipe with paper towel or cotton. You can always polish anytime; wipe away excess.
I've had DCC and DC locos/lash-ups creep at a scale 3-5MPH around the staging level loop 100' with NO STALL or FAULTER. gotta love it